Red Plague in Silver-Plated Conductors

The phenomenon of red plague becomes news in the wire and cable industry about every ten to fifteen years. It typically appears with a manufac- turer new to making high-tempera- ture silver-plated wire or silver-plated braid. Red plague occurs when the silver plating becomes damaged and is subject to moisture and/or high temperatures during the manufac- turing process. The technical term for red plague is cuprous oxide cor- rosion. It is typically visible as spots of red or brown on the silver-plated conductor or silver-plated braid.

Years ago,the term red plague was given to describe the red corrosion (cuprous oxide, Cu2O) or the black (cupric oxide, CuO) corrosion. The corrosion is caused by the electro- chemical reaction induced when a galvanic cell is formed between the copper conductor core and the sil- ver plating. Copper is higher on the galvanic series than silver, meaning that silver is more noble than cop- per. In the presence of moisture, the

copper will corrode.The corrosion of the copper conductor creates loss of the mechanical properties including strength and ductility. The corrosion can also cause degradation of the electrical conductivity. In the worst case observed, a silver-plated hook- up wire was cut in short six-inch pieces that caused the conductor to turn to a reddish powder that com- pletely poured out of the insulation.

Red plague was first investigated in depth by Anthony and Brown in a 1965 article in Materials Protection Magazine. It was found that in every case where corrosion was visible there was a corresponding break in the silver plating. But not every place where there was a break in the silver plating was corrosion present.To de- crease the chances of a gap in silver plating, a minimum plating thickness of silver is present in most wire speci- fications. Military specifications such as MIL-DTL-16878H and MIL-DTL-17J require a minimum plating thick- ness of 40 microinches (0.0001 mm). ASTM B298 includes tests for measur- ing the minimum plating thickness.

To prevent red plague, wire manu- facturers must keep equipment in a clean environment. Silver-plated raw material must be kept in a low-humidity environment (below 50 percent relative humidity). Most im- portantly, wire manufacturers should avoid mechanical abrasion of the sil- ver-plated conductor in the stranding and braiding process.

There have been several articles written about this red-plague phe- nomenon by NASA, ASTM, SAE, and

IPC. One of the most influential presentations was created by Rob- ert William Cooke at NASA in 2010 and is available at http://hdl.handle. net/2060/20100009723.

For questions or more informa- tion, contact your Anixter representa- tive or visit anixter.com.

Leave a Comment

Contact Us

We'd love to hear from you! Send us a quick note and we'll get back to you ASAP.

Not readable? Change text. captcha txt

Start typing and press Enter to search